乐泰® EA 9460™ is a thixotropic, modified, two-component epoxy adhesive formulated for ease of use as well for a good balance of properties. This two-part adhesive is formulated to give very high peel strength coupled with excellent shear strength. The flexibility of the cured adhesive makes it useful for bonding dissimilar substrates. Recommended substrates include metals, engineering thermoplastics, and thermoset laminates such as sheet molding compound (SMC) without the use of primers.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Resin:
Specific Gravity @ 25 °C 1.35
Viscosity, Brookfield - HB, 25 °C, mPa•s (cP):
Spindle 6, speed 20 rpm 150,000 to 300,000LMS
Weight Per Gallon, lbs/gal 11.3
Flash Point - See SDS
Hardener:
Specific Gravity @ 25 °C 1.31
Viscosity @ 25°C, mPa•s (cP) 100,000 to 250,000
Weight Per Gallon, lbs/gal 10.9
Flash Point - See SDS
Mixed:
Specific Gravity @ 25 °C 1.33
Viscosity @ 25°C, mPa•s (cP) 150,000 to 250,000
Peak Exotherm Temperature, °C, 93
Weight Per Gallon, lbs/gal 11.1
Pot life @ 25 °C, minutes 40 to 65LMS
TYPICAL PROPERTIES OF CURED MATERIAL
Cured @ 25 °C except where noted
Physical Properties:
Shore Hardness, ISO 868, Durometer D:
Cured for 2 hours @ 60 °C ≥75LMS
Glass Transition Temperature, °C 68
Elongation, ISO 527-2, % 3.5
Tensile Strength, ISO 527-2 N/mm2 30.3
(psi) (4,400)
Tensile Modulus, ISO 527-2 N/mm2 2,758
(psi) (400,000)
乐泰®EA 9460™是汤姆逊，改性，环氧胶粘剂的配方为两维草of use as well for a good balance of置业。这两方面是非常高的胶粘剂配方给皮强度耦合以及优秀的剪切强度。the Flexibility of the固化胶粘剂使它useful for接合异种基质。建议包括金属基质，工程thermoplastics，and thermoset laminates such as薄板成型复合（SMC）without the use of引物。
uncured材料的典型性能
树脂：
比重：25℃1.35
粘度，Brookfield，HB，25℃，mpa•s（CP）：
主轴6速20转300000lms 150000 to
体重每加仑，磅/加仑11.3 |
免责声明：以上所展示的信息由会员自行提供，内容的真实性、准确性和合法性由发布会员负责，www.qy6.com对此不承担任何责任。如有侵犯您的权益，请来信通知删除。