ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/ELECTRODAG 503-62%电子组装/工业胶水/电子组装胶水/工业用胶
技术服务热线：021-51693135 / 021-22818476
Electrodag™ 503 62%™ is a general purpose coating suitablefor direct application to most substrates including plastics andelastomers. It is designed to exhibit good resistance toultraviolet radiation, oxidation and corona.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Solids Content, % 16
Viscosity, Brookfield - LVT, mPa•s (cP):
Spindle 2, speed 12 rpm, Shake 5 minutes 1,700
Density, kg/l 1.75
Theoretical coverage, m2/kg:
@ 25μm 4.0
Shelf Life , from date of qualification in original seal, years 2
Flash Point oC 20
TYPICAL DRYING PERFORMANCE
Recommended Drying Conditions
15 minutes @ 150°C or
1 hour @ 25°C
Allow Electrodag™ 503 62%™ to dry at above temperatures prior to
soldering. The above drying profile is a guideline recommendation. Conditions(time and temperature) may vary based on customers' experienceand their application requirements, as well as customer dryingequipment, oven loading and actual oven temperatures. Storage Store product in the unopened container in a cool dry wellventilated area. Storage information may be indicated on theproduct container labeling.Optimal Storage: 5 to 20°C. Storage below 5°C or greaterthan 20°C can adversely affect product properties.
Electrodag™503 62％™是适用的通用涂层直接应用于大多数基材，包括塑料和弹性体。它被设计为表现出良好的抵抗力紫外线辐射，氧化和电晕。
固化材料的典型特性
固体含量％16
粘度，Brookfield - LVT，mPa&# |
 |
| |
|
|
 |
|
|
免责声明：以上所展示的信息由会员自行提供，内容的真实性、准确性和合法性由发布会员负责，www.qy6.com对此不承担任何责任。如有侵犯您的权益，请来信通知删除。