乐泰 HYSOL GR 2811 epoxy molding compound deliversoutstanding performance and ease of use.
This material isdesigned to achieve JEDEC Level 1 requirements, at 260°C eflow temperature.乐泰 HYSOL GR 2811 meets UL 94 V-0 Flammability at6.35mm thickness.TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 15Spiral Flow, @ 177°C, inches 34Shelf Life:@ -4oC, days 183TYPICAL PROCESS DATA
HandlingPreheat Temperature , °C 80 to 95Molding Temperature, °C 140 to 180Transfer Pressure, Kgf/cm2 40 to 85Transfer Time, seconds 6 to 15Curing Time, :@ 177oC, seconds 30 to 45Curing Time, 3 mm section:Conventional mold:@ 175oC, seconds 40 to 70
Automold:@ 175oC, seconds 30 to 60Post Cure @ 175°C, hours 2 to 6StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at -4oCor below, in closed containers.
After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisture
contamination. The suggested waiting time for a standard 15kg carton box is 24 hours.
乐泰 HYSOL GR 2811环氧树脂模塑料具有出色的性能和易用性。
该材料设计为在260°C达到JEDEC 1级要求回流温度.乐泰 HYSOL GR 2811符合UL 94 V-0可燃性在6.35mm厚度。
固化材料的特性特性时间@ 175°C，秒15螺旋流，@ 177°C，英寸34Shelf寿命：@-4oC，天183工艺数据处理预热温度，°C 80至95模具温度，°C 140至180转印压力Kgf /cm240至85转印时间秒6至15℃固化时间：177℃，秒30至45℃固化时间，3毫米截面：常规模具：@ 175℃秒40至70Automold：@175oC，秒30至60固化@ 175°C，小时2至6个储存在未开封的容器中的产品在干燥的位置。
储存信息可能在产品容器标签上指示。粉末储存 - 粉末或预制件应存放在 - 4oC以下，在密闭容器中。从冷藏箱中取出后，必须在密封容器中允许材料进入室温，以避免潮湿污染。
标准15kg纸箱的建议等待时间为24小时。 |
 |
|