乐泰 HYSOL KL 1000-3A provides the lowest cost ofownership with superior moldability and reliability.乐泰 HYSOL KL 1000-3A meets UL 94 V-0 Flammability at 3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 23Spiral Flow, @ 175°C, cm 80Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATA
HandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time: Conventional mold, seconds 10 to 18Automold, seconds 4 to 10Curing Time, @ 175oC: Conventional mold, seconds 50 to 120Automold, seconds 50 to 80Post Cure @ 175°C, hours 4 to 6乐泰 HYSOL KL 1000-3A has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.
Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown above.StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers. After removal from cold storage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15 kg carton box is 24 hours.
乐泰 HYSOL KL 1000-3A提供*低的拥有成本，具有出色的成型性和可靠性.乐泰 HYSOL KL 1000-3A符合UL 94 V-0易燃性厚度为3.175mm。
固化材料的特性特性时间@ 175°C秒秒23螺旋流@ 175°C cm 80Shelf寿命@5oC365天工艺数据处理预热温度：常规模具，°C 80至100Automold，秒0至5成型温度，℃150至195压铸压力，Kg /cm240至100转印时间：常规模具，秒10至18Auoldold，秒4至10℃时间，@175oC：常规模具，秒50至120Automold，秒50至80后固化@ 175°C，小时4至6乐泰 HYSOL KL 1000-3A已配制成尽可能提供可塑性和成型宽度。
尽管成型和固化条件将不同的情况，建议的起始范围如上所示。储存产品在未开封的容器中，在干燥的位置。储存信息可能在产品容器标签上指示。
粉末储存 - 粉末或预制件应存放在5oC以下，密闭容器中 |
 |
|