汉高汉高乐泰乐泰 Terophon HDF 6152
技术服务热线：021-51693135 / 021-22818476
TEROSON EV 6152 HDF is an EVA based thermoplastic material. Its primary function is to be designed in for use as an integral damping component at, or near, vibratory sources to dissipate energy through the transmission path. TEROSON EV 6152 HDF is a viscoelastic expandable, high damping foam exhibiting material damping loss factor above 1.1 in the targeted frequency range. Damping of
structure borne noise sources such as:
- Engine
- Suspension
- Exhaust system
- Accessories drives
APPLICATION AREAS
Closure panels, Hollow body network, Doors, Frame, Hoods, Engine and suspension cradles, Deck lids, Unibody network.
TECHNICAL DATA
(Typical Test Results)
Colour anthracite
Consistency solid
Odour weak, characteristic
Expansion > 450 to 700 % (depending on
sample dimension and curing
conditions)
Density at delivery 1.19 to 1.21 g/cm3
Corrosion resistance
on electro coated steel * no corrosion
on bare steel * no corrosion
Shear strength 0.3 to 0.5 MPa
layer thickness 3 mm
curing conditions 15 min at 175 °C
(object temperature)
In service temperature range -40 to 80 °C
480h 500ml/h 5% NaCl-solution / 35°C according to VDA 621-415
泰罗松EV 6152 HDF是基热塑性材料的伊娃。它的主要功能是设计用于作为一个整体的阻尼组件，或附近，振动源的能量耗散通过传输路径。泰罗松EV 6152 HDF是一种粘弹性可扩展、高阻尼聚氨酯泡沫材料的阻尼损耗因子在1.1以上的有针对性的频率范围。阻尼
技术数据
（典型测试结果）
颜色无烟煤
一致性固体
气味微弱，特征
扩展> 450到700%（取决于
试样尺寸和固化
条件）
密度1.21克/厘米1.19交付3
耐腐蚀性
电镀层钢无腐蚀
裸钢无腐蚀
剪切强度0.3至0.5兆帕
层厚度3毫米
固化条件15分钟在175°C
（物体温度）
在服务温度范围- 40至80°C
480h 500ml／h 5%的NaCl溶液/ 35°C根据VDA 621-41 |