乐泰 363平板电脑/笔记本ipad专用胶水，乐泰胶水
技术服务热线：021-51693135 / 021-22818476
乐泰® 363™ is designed for shallow potting and thin-film encapsulating of electronic assemblies. TYPICAL PROPERTIES OF UNCURED MATERIAL Specific Gravity @ 25 °C 1.1 Flash Point - See MSDS Viscosity, Brookfield - RVT, 25 °C, mPa•s (cP): Spindle 1, speed 20 rpm 100 to 400LMS TYPICAL CURING PERFORMANCE This product is cured when exposed to UV radiation of 365nm. To obtain a full cure on surfaces exposed to air, radiation at 250nm is also required. The speed of cure will depend on the UV intensity as measured at the product surface. Typical cure condition is 20-30 seconds at 100mW/cm2 using a medium pressure, quartz envelope, mercury vapor lamp. Tack Free Time Tack Free Time is the time required to achieve a tack free surface Tack Free Time, seconds: 100 mW/cm2, measured @ 365 nm 25 Fixture Time Fixture time is defined as the time to develop a shear strength of 0.1 N/mm2. UV Fixture Time, Glass microscope slides, seconds: 6 mW/cm2, measured @ 365 nm ≤15LMS 100 mW/cm2, measured @ 365 nm 5
乐泰®363™设计用于电子组件的浅灌封和薄膜封装。固化材料的典型特性25°C时的比重1.1闪点 - 参见MSDS粘度，Brookfield - RVT，25°C，mPa•s（cP）：主轴1，转速20 rpm 100至400LMS典型固化性能本产品固化当暴露于365nm的紫外线辐射。为了在暴露于空气的表面上获得完全固化，也需要在250nm的辐射。固化速度将取决于在产品表面测量的紫外线强度。典型的固化条件为：在100mW / cm 2的情况下，使用中压，石英外壳，汞蒸气灯，为20-30秒。无空闲时间粘贴时间是实现无粘性表面所需的时间无空闲时间秒秒：100毫瓦/厘米2，在365nm测量25夹具时间夹具时间定义为开发剪切强度为0.1N / mm2。 UV固定时间，玻璃显微镜载玻片，秒：6mW / cm 2，在365nm±15nm±100mW / cm 2下测量，在365nm |
免责声明：以上所展示的信息由会员自行提供，内容的真实性、准确性和合法性由发布会员负责，www.qy6.com对此不承担任何责任。如有侵犯您的权益，请来信通知删除。