乐泰 HYSOL KL 4000-1T epoxy molding compound deliversoutstanding performance and ease of use.乐泰 HYSOL KL 4000-1T meets UL 94 V-0 Flammabilityat 3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 25Spiral Flow, @ 175°C, cm 85Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, @ 175oC:Conventional mold, seconds 60 to 120
Automold, seconds 50 to 90Post Cure @ 175°C, hours 4 to 6Not for product specifications
The technical data contained herein are intended as referenceonly. Please contact your local quality department forassistance and recommendations on specifications for thisproduct.
StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers. After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination. The suggested waiting time for a standard 15 kg carton box is 24 hours.
乐泰 HYSOL KL 4000-1T环氧树脂成型复合材料具有出色的性能和易用性.乐泰 HYSOL KL 4000-1T符合UL 94 V-0 Flammabilityat 3.175mm厚度。
固化时间@ 175°C，秒25螺旋流，@ 175°C，cm 85Shelf寿命：@5oC，天365工艺过程数据处理预热温度：常规模具，80至100Automold，秒0至5模具温度，°C 150至195模压，Kg / cm 2 40至100转印时间：常规模具秒10至20Auoldold秒秒4至10℃恒定时间@ 175℃常规模具秒60至120Automold，秒50至90后固化@ 175°C，小时4至6不适用于产品规格本文包含的技术数据仅供参考。
请联系您当地的质量部门，了解本产品的规格。StorageStore产品在未开封的容器中，在干燥的位置。存储信息可能在产品容器标签上指示。粉末储存 - 粉末或预制件应存放在5oC以下，密闭容器中。
从冷藏箱中取出后，必须在密封容器中使材料达到室温，以避免水分污染。