ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/ACHESON PM-500电子组装/工业胶水/电子组装胶水/工业用胶
技术服务热线：021-51693135 / 021-22818476
PM-500 is designed to dry rapidly to form a flexible, conductivecoating. It is suitable for applications using high speedflexographic printing techniques.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Solids Content, % 82.5 to 84.0
Viscosity, Brookfield - RVT, mPa•s (cP):
Spindle 4, speed 20 rpm, @ 25oC 2,300 to 7,000
Density, kg/l 3,200
Theoretical coverage, m2/kg:
@ 25μm 5.74
Shelf Life @ 5 to 40°C (from date of manufacture),
months6
TYPICAL DRYING PERFORMANCE
Use high velocity hot air and/or infra-red systems for optimumperformance. Temperature settings depend on the substrate in useand process speed therefore drying rates should be determined basedon the temperature constraints of the substrate and production dryingcapability. The relationship between resistivity and drying temperatureis shown in the following graph. All samples were exposed to thetemperature indicated for a period of 1minute.
Storage
Store product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Optimal Storage: 5 to 40 °C
PM-500设计用于快速干燥以形成柔性，导电性涂层。适用于高速应用柔版印刷技术。
固化材料的典型特性
固含量，％82.5〜84.0
粘度，Brookfield - RVT，mPa•s（cP）：
主轴4，转速20 rpm，@25oC2,300〜7,000
密度，kg / l 3,200
理论覆盖率，m2/ kg：
@25μm5.74
保质期为5至40°C（自生产日期起）
几个月6
典型干燥性能使用高速热空气和/或红外系统进行*佳化性能。温度设 |