HYSOL GR360A(FC) 电子胶水/塑封胶水/汉高乐泰胶水/塑封方案
技术服务热线：021-51693135 / 021-22818476
乐泰 HYSOL GR 360A(FC) epoxy molding compounddelivers outstanding performance and ease of use.
乐泰HYSOL GR 360A(FC) epoxy molding compound contains nobromine, antimony or phosphorus flame retardant.乐泰 HYSOL GR 360A(FC) meets UL 94 V-0 Flammabilityat 6.35mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 23Spiral Flow, @ 175°C, cm 73.66Shelf Life:@ 5oC, months 12
Hot Hardness,Shore-D@ 175°C, 90 seconds 85TYPICAL PROCESS DATAHandlingPreheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:Conventional mold, seconds 10 to 20Automold, seconds 4 to 10Curing Time, :Conventional mold:@ 175°C, seconds 40 to 90
Automold:@ 175°C, seconds 20 to 60Post Cure @ 175°C, hours 4 to 6
乐泰 HYSOL GR 360A（FC）环氧树脂成型复合材料具有出色的性能和易用性。
乐泰HYSOL GR 360A（FC）环氧树脂模塑料含有无溴，锑或磷阻燃剂.
乐泰 HYSOL GR 360A（FC）符合UL 94 V-0 Flammabilityat 6.35mm厚度。固化材料的特性特性时间@ 175°C，秒23螺旋流，@ 175°C，cm 73.66Shelf寿命：@5oC，月12热硬度，肖氏-D @ 175°C，90秒85特殊工艺数据处理预热温度：常规模具，°C 80至100Automold，秒0至5模具温度，℃150至195模压，Kg / cm 2 40至100转印时间：常规模具秒10〜20Automold，秒4〜10℃时间：常规模具：@ 175℃，秒40〜90秒Automold：@ 175°C，秒20至60℃固化@ 175°C，4至6小时 |