汉高汉高乐泰乐泰 3707
技术服务热线：021-51693135 / 021-22818476
乐泰 3707 UV curable edgebond is designed for bonding various types of electronic components on a PCB.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, Brookfield CP52, 25 °C, mPa•s (cP):
Speed 20 rpm 9,595
Pot Life @ 25oC, days <7
Shelf Life - Refer to package label
Flash Point - See SDS
TYPICAL CURING PERFORMANCE
Recommended UV Cure
>3,000mJ or
>30 seconds @ 100 mW/cm2
Cure Depth, mm:
MPHL (UVALoc1000) at 100 mW/cm2, for 30 seconds ≥10
Oven Cure
2 minute @ 130°C
Minimum intensity of 100 mW/cm2 is recommended for the UV lamp. Use suggested cure schedules as general guidelines; other cure schedules may yield satisfactory results.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Specimen was prepared by thermal cure only
Physical Properties
Coefficient of Thermal Expansion , ppm/°C:
Below Tg 52
Above Tg 151
Glass Transition Temperature (Tg) by TMA, °C 53
Storage Modulus, GPa 4.4
乐泰3707 UV edgebond设计结合各类电子元件在PCB。
固化材料的典型性能
粘度，Brookfield cp52，25°C，MPA•S（CP）：
速度20转9595
锅生活@ 25oC、d＜7
货架寿命-参考包装标签
闪点-见SDS
典型的固化性能
推荐固化
> 3000mj或
> 30秒@ 100毫瓦/厘米2
固化深度，采购经理：
MPHL（uvaloc1000）在100毫瓦/厘米2，30秒≥10
烘箱中固化
2分钟@ 130°C
*小强度为100毫瓦/厘米2推荐用于紫外灯。使用建议的治疗时间表作为一般指导方针，其他治疗方案可能会产生令人满意的结果。
上述固化型材指南建议。固化条件（时间和温度）可能会根据客户的经验和他们的应用要求，以及客户固化设备，烘箱负荷和实际烤箱温度变化。
固化材料的典型性能
标本仅通过热固化制备
物理性质
热膨胀系数，PPM /°C：
在Tg 52
在Tg 151
玻璃化转变温度（Tg）通过TMA，°C 53
储能模 |