乐泰 5623平板电脑/笔记本ipad专用胶水，乐泰胶水
技术服务热线：021-51693135 / 021-22818476
乐泰® 5623™ is a two-component silicone that will cure at room temperature or at elevated temperatures. After mixing, the material cures quickly to form a clear, very flexible elastomer. TYPICAL PROPERTIES OF UNCURED MATERIAL Part A: Specific Gravity @ 22 °C 0.97 Viscosity, Brookfield, 25 °C, mPa•s (cP): Spindle 3, speed 50 rpm 600 to 1,000LMS Part B: Specific Gravity @ 22 °C 0.97 Viscosity, Brookfield, 25 °C, mPa•s (cP): Spindle 3, speed 50 rpm 600 to 1,000LMS Mixed: Specific Gravity @ 22 °C 0.97 TYPICAL CURING PERFORMANCE Gel Time Gel time, 25 °C, minutes 30 to 100LMS TYPICAL PROPERTIES OF CURED MATERIAL After 30 minutes @ 150 °C Physical Properties: Shore Hardness, ISO 868, Durometer OO 30 to 55LMS Cured for 72 hours @ 22 °C Physical Properties: Refractive Index 1.41 Coefficient of Thermal Conductivity ASTM F 433, W/(m•K) 0.15 Storage Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling. Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties.
乐泰®5623™是双组分硅胶，可在室温或高温下固化。混合后，材料快速固化，形成透明，非常柔软的弹性体。固化材料的典型特性部分A：比重@ 22°C 0.97粘度，布鲁克菲尔德，25°C，mPa•s（cP）：主轴3，转速50 rpm 600至1,000LMS部分B：比重@ 22°C 0.97粘度，布鲁克菲尔德，25°C，mPa•s（cP）：主轴3，转速50 rpm 600至1,000LMS混合：22°C比重0.97典型固化性能凝胶时间凝胶时间，25°C，30至100LMS固化材料的典型性能在150°C下30分钟后物理性能：肖氏硬度，ISO 868，硬度计OO 30至55LMS在22℃下固化72小时物理性能：折射率1.41导热系数ASTM F 433，W / （m•K）0.15储存将产品存放在未开封的容器中，干燥处。存储信息可能在产品容器标签上显示。*佳储存温度：8°C至21°C。低于8°C或高于28°C的储存可能会对产品性能产生不利影响。 |
免责声明：以上所展示的信息由会员自行提供，内容的真实性、准确性和合法性由发布会员负责，www.qy6.com对此不承担任何责任。如有侵犯您的权益，请来信通知删除。