乐泰 HYSOL GR 2220 epoxy molding compound deliversoutstanding performance and ease of use.TYPICAL PROPERTIES OF UNCURED MATERIALSpiral Flow, @ 175°C, inches 32Gel Time @ 175 °C, seconds 18Shelf Life @ 5°C (from date of manufacture), days 365 pecific Gravity, g/cm3 1.82TYPICAL PROCESS DATAHandlingMolding Temperature, °C 160 to 200Transfer Pressure, Kgf/cm2 40 to 80Transfer Time, seconds 5 to 15Curing Time, @ 180 °C, seconds 70 to 100Post Mold Cure @ 175 °C, hours 4 to 12Hot Hardness @ 175 °C 87乐泰 HYSOL GR 2220 has been formulated to provide the bestpossible moldability and as wide a molding latitude as possible.
Although molding and curing conditions will vary from situation tosituation, recommended starting ranges are shown above.
TYPICAL PROPERTIES OF CURED MATERIALAll measurements are taken at 175oC, unless otherwise noted.All physical, electrical and analytical measurements are taken onspecimens cured for 120 seconds @ 175°C with post cure of 6hours@ 175°C, unless otherwise specified.
Physical PropertiesGlass Transition Temperature, °C 161Coefficient of Thermal Expansion :
Below Tg, ppm/°C 18.5Above Tg, ppm/°C 63.3Conversions(°C x 1.8) + 32 = °FkV/mm x 25.4 = V/milmm / 25.4 = inchesN x 0.225 = lbN/mm x 5.71 = lb/inN/mm2 x 145 = psi
MPa = N/mm2MPa x 145 = psiN•m x 8.851 = lb•inN•m x 0.738 = lb•ftN•mm x 0.142 = oz•in
mPa•s = cP
乐泰 HYSOL GR 2220环氧树脂模塑复合材料具有出色的性能和易用性。
175℃，英寸32Gel时间175℃下的固化材料螺旋流动的特性特性：秒5秒（从制造日期起）比重，g /cm31.82特殊工艺数据处理模具温度，°C 160至200转印压力Kgf /cm240至80转印时间秒5至15℃固化时间，@ 180°C，秒70至100后模具固化175℃，小时4至12硬度@ 175°C 87乐泰 HYSOL |