乐泰 HYSOL KL 6500S epoxy molding compound deliversoutstanding performance and ease of use.
This material isdesigned to achieve JEDEC Level 1 requirements, at 260°Creflow temperature.
乐泰 HYSOL KL 6500S meets UL 94 V-0 Flammability at3.175mm thickness.
TYPICAL PROPERTIES OF UNCURED MATERIALGel Time @ 175 °C, seconds 28
Spiral Flow, @ 175°C, cm 110Shelf Life:@ 5oC, days 365TYPICAL PROCESS DATAHandling
Preheat Temperature :Conventional mold, °C 80 to 100Automold, seconds 0 to 5Molding Temperature, °C 150 to 195Molding Pressure, Kg/cm2 40 to 100Transfer Time:
Conventional mold, seconds 10 to 24Automold, seconds 4 to 15Curing Time, @ 175oC, seconds:Conventional mold, 60 to 120Automold, 50 to 90Post Cure @ 175°C, hours 4 to 6
StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.
Powder Storage - Powder or preforms should be stored at 5oCor below, in closed containers.
After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisturecontamination.
The suggested waiting time for a standard 15kg carton box is 24 hours.
乐泰 HYSOL KL 6500S环氧树脂模塑复合材料具有出色的性能和易用性。
该材料设计为在260°C达到JEDEC 1级要求回流温度.乐泰 HYSOL KL 6500S符合UL 94 V-0厚度为1.1775mm的可燃性。
固化材料的特性特性时间@ 175°C，秒28螺旋流，@ 175°C，cm 110Shelf寿命：@5oC，天365工艺流程数据处理预热温度：常规模具，℃80至100Automold，秒0至5模具温度，℃150至195压铸压力，Kg /cm240至100转印时间：
常规模具，秒10至24Automold，秒4至15固化时间，@175oC，秒：常规模具，60至120Automold，50至90固化175℃，小时4至6StorageStore产品在未开封的容器中，在干燥的位置。
存储信息可能在产品容器标签上指示。
粉末储存 - 粉末或预制件应存放在5oC以下，密闭容器中。
从冷藏箱中取出后，必须在密封容器中使材料达到室温，以避免水分污染。
标准15kg纸箱的建议等待时间为24小时 |