汉高汉高乐泰Ablestik 2332 HF
技术服务热线：021-51693135 / 021-22818476
乐泰 ABLESTIK 2332-17U is a solventless epoxy adhesive that develops high bond strength when cured at temperatures as low as 100 to 130°C.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity @ 25 °C, mPa∙s (cP) 100,000
Specific Gravity @ 25oC 1.16
Shelf Life @ 0 to 4°C, days 182
Flash Point - See SDS
TYPICAL CURING PERFORMANCE
Cure Schedule
1 hour @ 120°C
Alternative Cure Schedule
90 minutes @ 100°C
30 minutes @ 120°C
20 minutes @ 150°C
乐泰 ABLESTIK 2332-17U may also be cured in paint ovens at temperatures above 130oC.
The above cure profiles are guideline recommendations. Cure conditions (time and temperature) may vary based on customers' experience and their application requirements, as well as customer curing equipment, oven loading and actual oven temperatures.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Hardness, Shore D:
@ 25oC , minimum 75
TYPICAL PERFORMANCE OF CURED MATERIAL
Tensile Lap Shear Strength:
Al to Al :
@ 25°C N/mm2 24
(psi) (3,500)
乐泰 ABLESTIK 2332-17u是无溶剂环氧胶粘剂的粘接强度高，固化后形成在温度低至100到130°C.
固化材料的典型性能
粘度@ 25°C，MPA∙S（CP）100000
比重@ 25oC 1.16
保质期@ 0至4°C，天182
闪点-见SDS
典型的固化性能
治疗计划
1小时@ 120°C
替代治疗计划
90分钟@ 100°C
30分钟@ 120°C
20分钟@ 150°C
2332-17u 乐泰 ABLESTIK可固化油漆炉在130以上oC.温度
上述固化型材指南建议。固化条件（时间和温度）可能会根据客户的经验和他们的应用要求，以及客户固化设备，烘箱负荷和实际烤箱温度变化。
固化材料的典型性能
物理性质
Shore D硬度：
“25oC，*低75
固化材料的典型性能
拉伸搭接剪切强度：
铝对铝：
“25°C N / mm224
（PSI）（3500） |