乐泰® HHD 8600™ is a toughened, two component acrylic adhesive system designed with low halogen content for structural bonding and weld/rivet reduction. It is well suited for metal bonding applications where shock and impact resistance is required. The product cures very rapidly forming tough, resilient bonds. Once statically mixed, the two component acrylic cures at room temperature. Cure times can be reduced with the addition of mild heat to the bonded assemblies.
乐泰® HHD 8600™ is formulated with 0.127 mm spacers pre-dispersed within the adhesive to ensure that the adhesive bond area has adequate gap for optimal shock and impact performance. Typical applications include structural bonding of plastic and metal components that must withstand vibrations and impacts such as in portable devices and specialty vehicle markets.
TYPICAL CURING PERFORMANCE
Fixture Time
Fixture time is defined as the time to develop a shear strength of 0.1
N/mm2.
Fixture Time, ISO 4587, minutes:
Mild Steel 5 to 10
Peak Exotherm Temperature
Peak Exotherm Temperature, 10 gram mass:
Peak Temperature Time, minutes 11 to 22LMS
Peak Temperature, °C ≥212
乐泰®HHD 8600™是钢化、双组分丙烯酸粘合剂系统设计具有低卤素含量的结构粘接和焊接/铆钉还原。它非常适合于金属粘接应用的冲击和耐冲击性是必需的。该产品治愈非常迅速形成坚韧，弹性债券。一旦静态混合，两组分丙烯酸在室温下固化。固化时间可以减少与加入温和的热粘结组件。
乐泰®HHD 8600™是用0.127毫米的间隔预先制定的分散在粘合剂确保粘合区域有足够的间隙为*佳冲击性能。典型的应用包括塑料和金属部件的结构结合，必须承受振动和冲击，如在便携式设备和特种车辆市场。
固化材料的典型性能
部分：
比重@ 25°C 0.99
粘度，锥板，25°C，MPa（CP）：
物理MCR300 @剪切速率50 min-1的15000 35000lms
闪点-见SDS
B部分：
比重@ 25°C 0.97
粘度，锥板，25°C，MPa（CP）：
物理MCR300 @剪切速率50 min-1的15000 35000lms
闪点-见SDS
混合的:
比重@ 25°C 0.98
粘度，锥板，25°C，MPa（CP）：
锥cp50-1 @剪切 |