PRODUCT DESCRIPTIONHysol®MG15F-R is an anhydride cured molding compound designed for use in high voltage power applications requiringgood electrical stability at high temperature. The material isspecifically recommended for Power Discrete, High VoltageRectifier, and other applications where traditionally, Siliconemolding compounds have been the product of choice.PROPERTIES OF UNCURED MATERIALColor Black Spiral Flow, @ 177oC, cm 66Ram Follower Gel Time, seconds 8Shelf Life @ 5oC, months 12 TYPICAL CURED PROPERTIESAll measurements taken at 21oC unless otherwise noted. All
physical, electrical and analytical measurements taken onspecimens cured for two minutes at 190oC with post cure of 4hours at 200oC, unless otherwise specified.Glass Transition Temperature, °C, STP 65B 190Coefficient of Thermal Expansion, cm/cm/oC50o - 100oC, x 10-6 23250o - 260oC, x 10-6 71Specific Gravity 1.80Molded Shrinkage, as molded, % 0.5
Flexural Strength, kg/mm2 11.5Flexural Modulus, kg/mm2 1550Thermal Conductivity, CGS units, x 10-4 17Flammability Rating @ 3mm thickness V-0Moisture Absorption, 1 Atm steam, %100 hours 1.01000 hours 1.4Volume Resistivity, 500 volts, ohm-cm@ 21oC 1.5 x 1016@ 100oC 1.4 x 1015100 hours @ 15 psi 1.5 x 1016Water Extract Data, 1.5 hour water boil,conductivity, micromhos 20pH of extract 4.5chloride content, ppm 20sodium content, ppm 20HANDLINGMG15F-R has been formulated to provide the best possiblemoldability and as wide a molding latitude as possible.Although molding and curing conditions will vary from situation
产品描述Hysol®MG15F-R是酸酐固化的模塑料设计用于需要高温下良好电气稳定性的高压电源应用。该材料特别推荐用于Power Discrete，High VoltageRectifier以及其他传统上使用Siliconemolding化合物作为选择产品的应用.PRESSER OF UNCURED MATERIALColor Black螺旋流量，@177oC，cm 66Ram随机凝胶时间，秒8Shelf Life @5oC，月12典型固化性能除非另有说明，否则在21oC下进行所有测量。
所有物理，电气和分析测量取决于在190oC下固化2分钟，在200oC下后固化4小时，除非另有说明。玻璃转变温度°C，STP 65B 190热膨胀系数，cm / cm /oC50o-100oC，x 10 -623250o - 260oC，x 10-6 71特殊重力1.80模压收缩率，％0.5弯曲 |