3705 UV cure adhesive is designed for high throughput
assembly operations. Its thixotropic nature reduces migration
of the liquid product after application to the substrate.
TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, Brookfield - HBT, 25 °C, mPa•s (cP):
Spindle TB, Helipath, speed 10 rpm 44,000
Specific Gravity @ 25 °C 1.1
Flash Point - See MSDS
TYPICAL CURING PERFORMANCE
Recommended UV Cure
Light Source and Condition:
Zeta 7411 UV Flood System
Light Intensity, mW/cm2 30
UV Wavelength, nm 365
Time, seconds 80
3705 can be cured by exposure to UV and/or visible light of sufficient
intensity. Cure rate and ultimate depth of cure depend on light
intensity, spectral distribution of light source, exposure time, etc.
Fixture Time
UV fixture time is defined as the light exposure time required to
develop a shear strength of 0.1 N/mm2.
UV Fixture Time , Glass microscope slides, 0 gap, seconds:
6 mW/cm2, measured @ 365 nm ≤10 Storage
Store product in the unopened container in a dry location.
Storage information may be indicated on the product container
labeling.
Optimal Storage: 8 to 28°C. Storage below 8°C or greater
than 28°C can adversely affect product properties.
3705紫外线固化粘合剂设计用于高通量
装配作业。其触变性降低迁移
的液体产品。
固化材料的典型特性
粘度，Brookfield-HBT，25℃，mPa•s（cP）：
主轴TB，Helipath，转速10 rpm，44,000
25°C比重1.1
闪点 - 参见MSDS
典型的固化性能
推荐UV固化
光源及条件：
Zeta 7411紫外线防洪系统
光强度，mW /cm230
UV波长，nm 365
时间，秒80
3705可以通过暴露于足够的UV和/或可见光来固化
强度。治愈率和*极治疗深度取决于光
强度，光源光谱分布，曝光时间等
夹具时间
UV固定时间定义为所需 |