乐泰 HYSOL KL-G 500HT has been formulated to provide thebest possible moldability and as wide a molding latitude as possible.
Although molding and curing conditions willvary from situation tosituation, recommended starting ranges are shown above.TYPICAL PROPERTIES OF CURED MATERIALAll measurements taken at 25 °C unless otherwise noted.
All physical,electrical and analytical measurements taken on specimens curedfor 2 minutes @ 175 °C with post cure of 6 hours at 175 °C, unlessother wise specified.
Physical Properties:Coefficient of Thermal Expansion , ppm/°C:Below Tg 20Above Tg 60Glass Transition Temperature, °C 175Specific Gravity 2.2Molded shrinkage, as molded, % 0.24
Flexural ModulusKgf/mm2:@ 25 °C 1,400Flexural StrengthKgf/mm2:@ 25 °C 12Thermal Conductivity , W/(m-K) 1.92Water Extract Data, 90 minutes water boil:Conductivity, μmhos/cm 46pH of extract 7Extractable Ionic Content, ppm:Chloride (Cl-) 4Sodium (Na+) 15GENERAL INFORMATIONFor safe handling information on this product, consult the
Material Safety Data Sheet, (MSDS).
This product is not recommended for use in pure oxygenand/or oxygen rich systems and should not be selected asa sealant for chlorine or other strong oxidizing materials.Not for product specificationsThe technical data contained herein are intended as referenceonly. Please contact your local quality department for asistance and recommendations on specifications for thisproduct.StorageStore product in the unopened container in a dry location.Storage information may be indicated on the product containerlabeling.Powder Storage - Powder or preforms should be stored at 5oC orbelow, in closed containers. After removal from coldstorage, the material MUST be allowed to come to roomtemperature, in the sealed container, to avoid moisture
contamination. The suggested waiting time for a standard 15kg carton box is 24 hours.
乐泰 HYSOL KL-G 500HT已经配制成可提供*可能的成型性和尽可能宽的成型纬度。
虽然成型和固化条件可以从情况考虑，推荐的起始范围如上所示。
固化材料的特性所有测量在25 |
免责声明：以上所展示的信息由会员自行提供，内容的真实性、准确性和合法性由发布会员负责，www.qy6.com对此不承担任何责任。如有侵犯您的权益，请来信通知删除。